Tundish Upper Nozzle

Lintho	Nozzle e kaholimo		Nozzle e ka tlase		Hantle Block
	Zirconia core	Kantle	Zirconia core	Kantle
ZrO2+HfO2(%)	≥95		≥95
Al2O3(%)		≥85		≥85	≥85
MgO(%)					≥10
C(%)		≥3		≥3	≥12
Buik Density  g/cm³	≥5.2	≥2.6	≥5.1	≥2.6	≥2.6
Ho bonahala eka porosity  %	≤10	≤20	≤13	≤20	≤21
Matla a pshatlehang  Mpa	≥100	≥45	≥100	≥45	≥45
Ho hanyetsa mocheso oa mocheso	≥5	≥5	≥5	≥5

Sephutheloana:
1. Maemo a machaba a khonang ho romeloa ka ntle ho leoatle a paka.
2. Pallet ea lehong.
3. Lepolanka / mokotla oa bamboo (lebokose).
4. Boitsebiso bo eketsehileng ba ho paka bo tla itšetleha ka litlhoko tsa bareki.

Bohloeki ba rona bo phahameng le botenya ba ZrO2 tundish nozzle e na le botsitso bo botle ba ho ts'oha, khanyetso e matla ea khoholeho, nako e tšoarellang ea ho sebetsa joalo-joalo. Re na le sekhahla se phahameng sa 5.4g/cm3, re nka thepa e khethehileng le theknoloji, lisebelisoa tsa tlhahiso ea othomathike, nako e lekaneng ea ho thunya, ebe thepa e ntle ho feta bona. Bakeng sa li-nozzle tsa tundish, re etsa liteko ho 150tons ladle bakeng sa lihlahisoa tsa zirconia tse 95%, nozzle ea rona ea tundish e ka tsoela pele ho sebetsa lihora tse 10-12, le ho feta.
LBH
P: U ka laola boleng ba hau joang?
A: Bakeng sa ts'ebetso e 'ngoe le e' ngoe ea tlhahiso, Re na le sistimi e felletseng ea QC bakeng sa sebopeho sa lik'hemik'hale le thepa ea 'mele. Kamora tlhahiso, thepa eohle e tla lekoa, 'me setifikeiti sa boleng se tla romelloa hammoho le thepa.

P: O ka fana ka Mohlala?
A: Mohlala ke mahala bakeng sa hau setokong ntle le hore o lefelle litšenyehelo tse hlakileng.

P: Nako ea hau ea ho tsamaisa ke efe?
A: Hangata e hloka matsatsi a 15- 20 ka mor'a ho amohela PO.