Nkọwa
Ihe mejupụtara brik silica, dị ka aha ahụ na-egosi, bụ nke SiO2 mebere nke ọma (pasent uka dị n'elu 93%). Ọrụ okpomọkụ dị elu nke brik silica na-adabere na ọdịnaya SiO2, ọdịnaya adịghị ọcha, ihe ndị nwere ịnweta na ihe ndị ọzọ. Ọdịnaya SiO2 dị elu, mgbake dị elu nke brik Silica. Ngwakọta mineral nke brik silica bụ tridymite, cristobalite, quartz fọdụrụnụ na oge iko. A na-emechi ihe eji eme brik silica metụtara mgbanwe nke SiO2 crystalline.
Atụmatụ:
1. Low nnukwu njupụta,
2. Low thermal conductivity,
3. High pụtara porosity,
4.Good thermal ujo eguzogide,
5.Great elu okpomọkụ n'ibu ike,
6.High okpomọkụ kwụsie ike olu mgbanwe,
7.Strong acid slag ozize na-eguzogide.
Nkọwapụta
| Ihe |
Brick silica |
Brick silica |
| Igwe ọkụ ọkụ |
Igwe ọkụ ọkụ |
| Al2O3% |
≤1.5 |
≤0.5 |
| Fe2O3% |
≤1.5 |
≤0.8 |
| SiO2% |
≥94.5 |
≥96 |
| K2O+Na2O % |
CaO≤2.5 |
CaO≤2.5 |
| Refractoriness RºC |
≥1650 |
≥1650 |
| Ntugharị n'okpuru Ibu KD ºC |
KD≥1650 |
KD≥1650 |
| Mgbanwe ahịrị na-adịgide adịgide % (1450ºC×2h) |
0~+0.2 |
0~+0.2 |
| Prọsity pụtara % |
≤22 |
≤24 |
≤21 |
| Nnukwu njupụta g/cm3 |
≤2.33 |
≤2.34 |
≤2.34 |
| Oyi na-etipịa ike Mpa |
≥40 |
≥35 |
≥35 |
| 0.2MPa ọnụego na-akpụ akpụ% |
Quartz fọdụrụnụ ≤1.0% |
≤1.0% |
| Mgbasa ọkụ (1000ºC) |
≤1.28 |
≤1.30 |
/ |
| Ngwa |
N'okpuru na mgbidi |
Regenerator Bottom na Wall |
Igwe ọkụ ọkụ |
FAQ
Ajụjụ: Ị bụ ụlọ ọrụ azụmaahịa ma ọ bụ onye nrụpụta?
A: Anyị na-emepụta dị na China. Ndị ahịa anyị niile si n'ụlọ ma ọ bụ ná mba ọzọ, na-anabata nke ọma ileta anyị.
Ajụjụ: Gịnị bụ uru gị?
A: Anyị na-emepụta ihe, na anyị nwere ọkachamara mmepụta na nhazi na ahịa teams.Quality nwere ike na-ekwe nkwa.We nwere ọgaranya ahụmahụ na ferroalloy ubi.
Q: Gịnị bụ gị mmepụta ike na nnyefe ụbọchị?
A: 3000MT / ọnwa&Bupu n'ime ụbọchị 20 mgbe ịkwụ ụgwọ.
Ajụjụ: Ọnụ ahịa a ga-akwụ ụgwọ?
A: Ee, biko nweere onwe gị ịkpọtụrụ anyị oge ọ bụla ma ọ bụrụ na ị nwere ajụjụ ọ bụla. Maka ndị ahịa chọrọ ịbawanye ahịa, anyị ga-eme ike anyị niile ịkwado.
.jpg)
.jpg)
.jpg)
.jpg)
.png)